Take A Free ASNT NDT VT Level 2 Exam Practice Test – Quiz Course

by

Here You Can Take a Free Online ASNT NDT VT Level 2 Exam Practice Test with the latest Visual and Optical Testing Method level II Question and Answers

1.

Embrittlement, caused by a physical or chemical change in the metal is a reduction in:

 
 
 
 

2.

A discontinuity typically found in forgings is:

 
 
 
 

3.

Weldments might contain:

 
 
 
 

4.

During the solidification of metal, a hole produced due to escaping gases is called a:

 
 
 
 

5.

A convex weld surface:

 
 
 
 

6.

The fillet weld size is based on the:

 
 
 
 

7.

Service-induced discontinuities in bolting systems may be produced by:

 
 
 
 

8.

Discontinuities that are produced during the hot or cold working of the ingot into rod or bar to make studs are called:

 
 
 
 

9.

The least common location for fastener failure is:

 
 
 
 

10.

Localized reduction in an area of a bolt that is under overload conditions is referred to as:

 
 
 
 

11.

The deterioration of a metal by chemical or electrochemical reaction with its environment is called:

 
 
 
 

12.

The roughest surface finish is indicated by measurement of:

 
 
 
 

13.

A basic metallurgical joint configuration that is used for complete joint penetration is called:

 
 
 
 

14.

The welding process that is sometimes referred to as “stick welding” is:

 
 
 
 

15.

The welding process in which there is a high degree of probability of entrapping slag is:

 
 
 
 

16.

Tungsten inclusions are found during:

 
 
 
 

17.

The portion of base metal that has not been melted but where mechanical properties or microstructure have been altered by the heat of welding is defined as:

 
 
 
 

18.

The difference between discontinuities and defects is that:

 
 
 
 

19.

The gage that provides measurements of internal misalignment on 76 mm (3 in.) diameter pipe is:

 
 
 
 

20.

In a borescope, the image is brought to the eyepiece by:

 
 
 
 

21.

In welding, temperature-indicating sticks are used to monitor:

 
 
 
 

22.

To measure the diameter of a 76 mm (3 in.) stud most accurately, use:

 
 
 
 

23.

A discontinuity that appears as a series of remelted dots beside a weld, resembling a trail left in striking a match is called:

 
 
 
 

24.

A protrusion or rollover of weld metal beyond the toe or root is called:

 
 
 
 

25.

Chevrons may occur in:

 
 
 
 

26.

A discontinuity that is found in bars and forgings, which is caused by the rupture of metal forged at either too low or too high temperatures, is called:

 
 
 
 

27.

A cause for undercut that occurs during the welding process is called:

 
 
 
 

28.

When the weld is to be placed on the arrow side of the joint, the weld symbol in the drawing will be:

 
 
 
 

29.

The brazing process is commonly defined as a liquid-solid phase joining method accomplished at a temperature above:

 
 
 
 

30.

To be acceptable, a concave fillet weld must have an actual leg dimension that is:

 
 
 
 

31.

The melting and fusing of the filler metal and base metal into a straight continuous weld pass is called a:

 
 
 
 

32.

A depression on the face of a fillet weld that reduces the cross-section of the weld when measured at the depression is called:

 
 
 
 

33.

When visually examining an arc strike, the inspector should inspect for:

 
 
 
 

34.

Pitting is one type of:

 
 
 
 

35.

Joint profiles of finished welds are controlled by:

 
 
 
 

36.

Which of the following weld symbols represents a fillet weld?

Which-of-the-following-weld-symbols-represents-a-fillet-weld.png

 
 
 
 

37.

Which of the following weld symbols represents a U Joint?

Which-of-the-following-weld-symbols-represents-a-fillet-weld.png

 
 
 
 

38.

Electronic aids to vision are based primarily on:

 
 
 
 

39.

In order to obtain light of a specific wavelength, use:

 
 
 
 

40.

The three physical characteristics of color include:

 
 
 
 

41.

Horizontal indications on the edge of a 76 mm (3 in.) plate are on several levels and do not extend along the whole edge. The most likely cause of these visual indications is:

 
 
 
 

42.

A process that uses a filler metal with a liquidus state that does not exceed 449 °C (840 °F) and that does not melt the base material is:

 
 
 
 

43.

The angle(s) for the fore-oblique direction of the view borescope is/are:

 
 
 
 

44.

The mechanism for soldering and brazing is:

 
 
 
 

45.

A rounded discontinuity that occurs in the weld and is then distributed in line, parallel with the weld is called:

 
 
 
 

46.

A wide angle of view for a borescope provides:

 
 
 
 

47.

An optical aid used in visual examination that brings the image to the eyepiece by a lens train is called:

 
 
 
 

48.

A remote visual examination aid that is used for viewing around corners with a flexible distal end is called:

 
 
 
 

49.

An inherent discontinuity associated with the original solidification of metal in the ingot is called:

 
 
 
 

50.

Discontinuities associated with the casting process are:

 
 
 
 

51.

A narrow-angle of view in a borescope is required for:

 
 
 
 

52.

Which of the following is a primary processing method?

 
 
 
 

53.

A reduction in ductility due to in-service or pre-service environments is called:

 
 
 
 

54.

Metals that become weaker due to continuing deformation under steady stress at elevated temperatures demonstrate:

 
 
 
 

55.

Which of the following is a basic joint configuration?

 
 
 
 

56.

A nonfusion discontinuity that is located at the root area of a welded joint is called:

 
 
 
 

57.

In the casting process, a chaplet is:

 
 
 
 

58.

The three stages of fatigue are:

 
 
 
 

59.

Discontinuities that originate during the melting and original solidification of the metal in the ingot are categorized as:

 
 
 
 

60.

A welding process in which shielding is provided by the electrode covering is called:

 
 
 
 

61.

A slag-type discontinuity is produced by:

 
 
 
 

62.

Weld metal that completely fills the groove and is fused to the base metal throughout its total thickness is called:

 
 
 
 

63.

All casting discontinuities are considered to be:

 
 
 
 

64.

A disadvantage of the GMAW process is:

 
 
 
 

65.

A condition of excessive offset of the inside diameter surface is called:

 
 
 
 

66.

Failure to adequately penetrate the weld root of a groove weld is called:

 
 
 
 

67.

Repeated fluctuating stress having a maximum value less than the tensile strength of the material is called:

 
 
 
 

68.

Cracks can occur in:

 
 
 
 

69.

The structure or shape of mechanical fatigue-type cracking is best described as:

 
 
 
 

70.

The fundamental reason that a bimetallic thermometer operates is:

 
 
 
 

71.

Recording information from a visual examination is accomplished using:

 
 
 
 

72.

One of the principal characteristics of a hanger is that the:

 
 
 
 

73.

On a welding symbol, the flag symbol indicates:

 
 
 
 

74.

A crater crack is formed:

 
 
 
 

75.

A visual examination of the rubber elastomer seating material is performed on:

 
 
 
 

76.

The leg of a concave fillet weld is:

 
 
 
 

77.

An overload condition of component support is indicated by:

 
 
 
 

78.

A common processing discontinuity for a bolt is:

 
 
 
 

79.

The type of corrosion that occurs when dissimilar metals are in contact or are electrically connected in a corrosive medium is called:

 
 
 
 

80.

A mechanical device that controls flow is called:

 
 
 
 

81.

A visual examination of a swing check valve would include:

 
 
 
 

82.

The component support that allows normal thermal movement but restrains movement during a seismic event is called a:

 
 
 
 

83.

An employer shall establish a qualification and certification program based on:

 
 
 
 
 

84.

The most common location for fastener failure is:

 
 
 
 
 

85.

On a welding symbol, the horizontal line connecting the arrow and the tail are called the:

 
 
 
 

86.

Operationally, valves are categorized as linear and:

 
 
 
 

87.

A destructive force that occurs in components is:

 
 
 
 

88.

The formation and collapse of gas bubbles in fluids are called

 
 
 
 

89.

A restraint:

 
 
 
 

90.

A typical inadequate construction practice involving component supports in volve:

 
 
 
 

91.

Excessive clearance in gate valve guide ribs may lead to:

 
 
 
 

92.

For a given size weld, the theoretical throat for a concave fillet weld is:

 
 
 
 

93.

A device that transmits the load from a piping system to the building structure is called:

 
 
 
 

94.

The gage that is typically used to measure the face reinforcement of a butt joint is:

 
 
 
 

95.

Primarily, piping leaks occur at components such as:

 
 
 
 
 

96.

A hanger assembly that is attached to a pipe with a pipe clamp is considered to be:

 
 
 
 

97.

The theoretical throat dimension for a 10 mm (0.4 in.) leg fillet weld is:

 
 
 
 

98.

Overlap is a weld profile condition where the angle formed at the junction between the weld and base material is:

 
 
 
 

99.

A service-induced failure for component support could be caused by:

 
 
 
 
 

100.

Visual inspection is easy to apply, quick and relatively inexpensive and requires no special equipment other than:

 
 
 
 

101.

The human eye cannot always distinguish clearly the fine differences between contact angles and states of wetting when inspecting soldered joints. To improve the inspector’s ability to distinguish these differences, it is recommended that the inspector use magnification in the range of:

 
 
 
 

102.

Direct visual examination is possible when the eye can be placed within:

 
 
 
 

103.

During the performance of a visual examination, the borescope is used to:

 
 
 
 

104.

During the typical operation of a fiberoptic borescope, adequate lighting:

 
 
 
 

105.

Visual examination tools that use flexible glass strands to transfer the image are called:

 
 
 
 

106.

When an ingot is rolled, a lamination can result if it contains piping or:

 
 
 
 

107.

During the visual examination of forging, a folded thin flap of metal was observed. This is typically called:

 
 
 
 

108.

Arc strikes are typically caused by:

 
 
 
 

109.

The heat-affected zone is the portion of the:

 
 
 
 

110.

The most critical part of any weld is:

 
 
 
 

Question 1 of 110

Are You Looking for a Free ASNT NDT VT Level 2 Exam practice test?

Free ASNT NDT VT Level 2 Exam Practice Test
Take A Free ASNT NDT VT Level 2 Exam Practice Test – Quiz Course

If your answer is yes then you are at the right website. Here You Can Take a Free Online ASNT NDT VT Level 2 Exam Practice Test and Improve Your ASNT VT Level 2 – Visual and Optical Testing Method Exam Score. Here You Can Learn everything you need to know about ASNT VT Level II quickly and easily.

In This Practice test, We are covering the Latest ASNT VT Level 2 – Visual and Optical Testing Method Question and Answers, After completing the last Question you will see the ASNT VT Level II Practice Test Answer Key, No cheating now! Once you complete the test and check your answers please leave us your score and any comments in the comments section below

We will help you to pass the ASNT VT Level II Exam on the first attempt —99% Guaranteed. Our expert-written ASNT VT Level II – Visual and Optical Testing Method Examination practice material covers the actual exam topics with fully explained answers.

Take unlimited free ASNT VT Level II Quiz Course tests of any length. We have free Latest questions updated every week and you can study our material along with any other study materials.

If You Want to Buy Latest ASNT VT Level II Exam Self Study Material, Please Feel Free to contact us.

Buy ASNT VT LEVEL 2 Exam Learning Package Study Material
FOR EVERY 10 QUESTIONS 1 QUESTION COMES INTO THE EXAM
WE HAVE LATEST ASNT VT Level II -Visual and Optical Testing Method QUESTION BANK
Total 2000+ nos QUESTION BANK FROM THEORY TO PRACTICAL TO NUMERICALS.
Cost: $25.00
Email Us To Buy: upweld.org@gmail.com
Click Here To Contact us On Whatsapp https://wa.link/4dn6ee
Ideally, the only material needed for passing the examination. Free guidelines during learning.
We give you a lot of additional study material Free of cost with this question bank.
Get BOTH Formats Instantly:
Online—Instant scoring, review & reporting.
Printable—Instant download.

Take A Free ASNT LEVEL III Exam Practice Test
Latest LPT Level III Question and Answers Latest MT Level III Question and Answers
Latest RT Level III Question and Answers Latest UT Level III Question and Answers
Latest ASNT BASIC LEVEL III Question and Answers Latest VT Level III Question and Answers

If you want to get ASNT VT Level II – Visual and Optical Testing Method Training and Certification, Please feel free to contact us. 

Leave a Reply