AWS CWI Part A – WIT Welding Inspection Technology Chapter 9 – Weld and Base Metal Discontinuities- Latest 19 Question and Answers

1.

A discontinuity is:

 
 
 
 

2.

Whether a particular weld discontinuity is critical can be judged on the basis of:

 
 
 
 

3.

What discontinuity is generally considered to be the most severe?

 
 
 
 

4.

Which of the following discontinuities is less likely to be found visually?

 
 
 
 

5.

Underbead cracks can result from which of the following welding practices?

 
 
 
 

6.

The weld discontinuity that results from improper termination of the welding arc is referred to as:

 
 
 
 

7.

Of the following processes, which is unlikely to have slag inclusions in a completed weld?

 
 
 
 

8.

The discontinuity that results from the entrapment of gas within the weld cross-section is referred to as:

 
 
 
 

9.

What weld discontinuity results when the welder travels too slowly, causing excess weld metal to flow out of the joint and lay on the base metal surface without fusing?

 
 
 
 

10.

What weld metal discontinuity results when the welder fails to completely fill the weld groove?

 
 
 
 

11.

Excessive weld metal buildup on a groove weld is referred to as:

 
 
 
 

12.

The weld discontinuity that results from the initiation of the welding arc outside the weld joint is referred to as:

 
 
 
 

13.

What weld discontinuity shows up as a light region on a radiograph?

 
 
 
 

14.

Which of the following is a base metal discontinuity that is associated with the stresses induced from welding?

 
 
 
 

15.

What discontinuity is shown by #12b?

Questions Q9-15 through Q9-19 refer to the figure shown below:

Questions-Q9-15-through-Q9-19-refer-to-the-figure-shown-below

 
 
 
 

16.

What step-like discontinuity is shown by #11?
Questions-Q9-15-through-Q9-19-refer-to-the-figure-shown-below

 
 
 
 

17.

What discontinuity is shown by #12g?

Questions-Q9-15-through-Q9-19-refer-to-the-figure-shown-below

 
 
 
 
 

18.

What discontinuity is shown by #5?

Questions-Q9-15-through-Q9-19-refer-to-the-figure-shown-below

 
 
 
 
 

19.

What discontinuity is shown by #10?

Questions-Q9-15-through-Q9-19-refer-to-the-figure-shown-below

 
 
 
 
 


 

Click Here To Take The Next WIT Chapter 10>>

99% Passing Guarantee- If you Want to Purchase a Full AWS CWI Course Study Material Please Contact us.
AWS CWI Part A – WIT Welding Inspection Technology Chapter 9 – Weld and Base Metal Discontinuities- Latest 19 Question and Answers

 

#CertifiedWeldingInspectors
#CwiPartA
#WIT

For business inquiries: upweld.org@gmail.com
Follow us on Facebook https://www.facebook.com/UpWeld/
Follow us on Twitter https://twitter.com/upweldorg

AWS CWI Part A,
AWS Welding Inspection Technology Chapter 9,
Weld and Base Metal Discontinuities Questions and Answers
WIT Chapter 9 Latest Question and Answers,
Welding Inspection Technology Chapter 9 Questions and Answers,
AWS CWI Questions and Answers (Module 9)
Module 9 AWS CWI QUESTIONS ANSWERS
Chapter 9 practice test.
Welding Defects MCQ
what weld metal discontinuity results when the welder fails to completely fill the weld groove?
a discontinuity that is not associated with welds is
a discontinuity that is not associated with welds is mcq
whether a particular weld discontinuity is critical can be judged on the basis of:
base metal discontinuity associated with the stresses induced from welding is
cwi exam questions and answers pdf
excessive weld metal buildup on a groove weld is referred to as
which weld metal discontinuity is generally considered to be the most
CWI Fundamental technology Questions and Answers
QC Welding Inspector Interview Questions
welding inspection technology pdf free download
welding inspection technology 2008
what weld metal discontinuity results when the welder fails to completely fill the weld groove?
excessive weld metal buildup on a groove weld is referred to as
underbead cracks can result from which of the following welding practices?
base metal discontinuity associated with the stresses induced from welding is
which weld metal discontinuity is generally considered to be the most severe
the problem occurring in weldments due to the non-